FJ-C640 series fluorocarbon coating for solar PET film

140
Product description

Introduction

On the basis of PVDF series hot setting fluorocarbon coatings, Shanghai Fuleda Fluorocarbon Material Co., Ltd has developed FJ-H700 series fluorocarbon coatings, which are applicable to coiled material. FJ-H700 series is produced in accordance with USA AAMA2605 standards and GB/T17748, with coating performance and workability reaching to international standards of similar products.

FJ-H700 series fluorocarbon coatings adopt high-quality PVDF fluorocarbon resin which is made at home and abroad, with out-door weather resistance of more than 20 years. Content of PVDF resin in PVDF is more than 70%. The coating adopts inertia ceramic inorganic pigment, which is dedica-ted fluorocarbon coating for precoat coil.

 

Application Fields:

Galvanized steel coil, aluminium alloy coil, aluminizing zinc coil, coating coil and coating steel plate.

 

Process Parameters:

Name Base coat

Top coat

Finish coat

Product No.

FJ-H700A

FJ-H700

FJ-H700B

Appearance

Light gray dispersion liquor

Various colorful dispersion liquor

Semitransparent dispersion liquor

Fineness

≤20μm

≤25μm

≤25μm

Viscosity(coat-4/S)

90-120s

90-120s

90-120s

Solid content(Wt%)

≥50%

Solid≥55%
Metal≥45%

≥45%

Spreading rate(㎡/㎏)

27,10μm photopolymer

20.0,15μm photopolymer

22,10μm photopolymer

Thinner

X-16

X-16

X-16

Dilution ratio(coating/thinner)

5%-20%

5%-20%

5%-20%

Coating viscosity (coating 4# cup)

70-90s

70-90s

70-90s

curing temperature(PMT)

160-180℃,60s

220-250℃,60s

220-250℃,60s

 

Coating Process Description:

Since the adhesion force between FJ-H700 series fluorocarbon coatings and the processed coated steel plate and coated aluminum sheet are both outstanding, it is required to render by using FJ- H700A priming coating.

Since it will produce a lot of smog while baking, pay attention to exhaust.

Generally, in order to get right viscosity, it is required to dilute FJ-H700 series fluorocarbon coatings by using matched dedicated thinner before use.

 

Coating requirements::

FJ-H700 series fluorocarbon coatings have well applicability, which can meet requirements of coating speed at 10-60m/min on assembly line. FJ-H700 series fluorocarbon coatings are applicable to both steel roller and plastic roller equipment.

 

Packaging and Supplying:

The packaging of FJ-H700 series fluorocarbon coating all adopts metal drum. The specifications are as follows:

Base coat, top coat, finish coat

20㎏/barrel

Thinner

16㎏/barrel

 

The order for goods shall be carried out in accordance with Fuleda color card, without minimum order quantity requirement. The minimum order quantity for top coat, matching priming order and finishing coat according to other companies’ samples is 20kg, with delivery period being 2-5 days (free of transportation time).

Scan the QR code to read on your phone
We could not find any corresponding parameters, please add them to the properties table
Previous
Next

CONTACT INFORMATION

Western city hui Industrial Park, Chengyang District, Qingdao

OFFICIAL ACCOUNTS

ONLINE MESSAGE

Username used for comment:
Customer message
Description:
验证码